GT Products ” 6142 is an economical room- temperature curing silicone rubber compound. GT Products ” 6142 is designed for uses where optimum physical properties are not required.
GT Products ” 6142 features:
| x | Medium cost |
|---|---|
| x | Low durometer |
| x | Low viscosity |
| x | Resistance to sulfur clays |
GT Products ” 6142 is supplied in matched kits with Catalyst 6142 designed to be used in a
10:1 ratio by weight.
Because pigments can settle during storage, Catalyst 6142 should be thoroughly stirred before mixing. Use separate tools for mixing the base and catalyst to avoid cross contamination. Low-shear mixing of the mixture is recommended. Add the catalyst to the base and mix until the color is uniform. Use clean tools and scrape the bottom and sides of the container to assure a homogeneous mixture.
Base Catalyst
Color White Purple Specific Gravity 1.13 0.98 Viscosity (cPs) 45,000 100 Pot Life (pour time) 60-90 min.
After cure (7 days @ 25°C)
Tensile, psi: 500 Elongation, % 400 Durometer, Shore A 20 Tear (die B) 110 Linear shrinkage;%: 0.3-0.4
Air entrapped during mixing should be removed to prevent voids in the cured product. Deair the mixed material under a vacuum of 25 mm (29 inches) of mercury. The mixture will froth and, expand four times its volume, crest and recede to about the original level as the bubbles break. Degassing is usually complete about two minutes after frothing subsides.
GT Products ” 6142 will cure sufficiently in 16 hours at room temperature (75°F) to be handled. GT 6142 will reach 90% of ultimate cure in 24 hours at room temperature. For full cure an additional 1-2 days at room temperature is required.
GT Products ” 6142 will remain useful for six months when stored in the original unopened containers at temperatures below 80°F (27°C). Both GT Products ” 6142 and catalyst-6142 are sensitive to moisture. Keep containers covered.
GT Products ” 6142 is a condensation (“Tin catalyst”) cure system. It will cure in contact with most clean dry surfaces. GT Products ” 6142 will cure in contact with materials such as butyl and chlorinated rubbers, sulfur-containing materials, amines and other condensation RTV silicones which would inhibit the cure of addition-cure RTV rubber.
The above information is based on typical experience and should not be used for specification writing. Suitability of this product for a specific application should be determined under actual use conditions. No warranty, either expressed or implied, is hereby made.
January 2008